Compared with the materials of components, the materials of any element of the friction pair bear more severe loads. The relative motion between the friction pairs intensifies the effect of the load; the high temperature generated by the relative motion also promotes the process of change from the physical and chemical aspects. The speed of this change caused by the relative motion and interaction of the surface is much faster than the change caused by other behaviors in the component. Therefore, in tribological analysis and tribological design, a full life cycle analysis is necessary.
1. Corrosion risk stage
Before any new friction pair is put into operation, there is a storage and transportation stage. During this stage, the friction pair will inevitably come into contact with the atmospheric medium and will inevitably be affected by the external environment.
Before any new friction pair is put into operation, there is a storage and transportation stage. During this stage, the friction pair will inevitably come into contact with the atmospheric medium and will inevitably be affected by the external environment.
Good storage and transportation environment;
Appropriate anti-corrosion measures, such as anti-rust oil, vacuum packaging, etc.;
Try not to destroy these protective measures before they are put into use.
Appropriate anti-corrosion measures, such as anti-rust oil, vacuum packaging, etc.;
Try not to destroy these protective measures before they are put into use.
2. Running-in and wear stage
Running-in is the initial stage of contact and interaction between the friction pairs. In the early stage of operation of a new friction pair, due to the large surface roughness value of the dual surface, small effective contact area, small number of contact points and large area of most contact points, the contact points are severely adhered, so the wear rate is large. However, as the running-in progresses, the surface micro-convexities are gradually worn away, the surface roughness value decreases, the effective contact area increases, the number of contact points increases, and the wear rate decreases, creating conditions for the stable wear stage.
Running-in is the initial stage of contact and interaction between the friction pairs. In the early stage of operation of a new friction pair, due to the large surface roughness value of the dual surface, small effective contact area, small number of contact points and large area of most contact points, the contact points are severely adhered, so the wear rate is large. However, as the running-in progresses, the surface micro-convexities are gradually worn away, the surface roughness value decreases, the effective contact area increases, the number of contact points increases, and the wear rate decreases, creating conditions for the stable wear stage.
In order to avoid damaging the friction pair during the running-in wear stage, the running-in wear stage is mostly carried out under empty or low load;
In order to shorten the running-in time, lubricating materials containing additives and solid lubricants can also be used to run-in under a certain load and higher speed;
After the running-in is completed, it should be cleaned and replaced with a new lubricant.
In order to shorten the running-in time, lubricating materials containing additives and solid lubricants can also be used to run-in under a certain load and higher speed;
After the running-in is completed, it should be cleaned and replaced with a new lubricant.
3. Stable wear stage
In this stage, the wear is slow and stable, and the wear rate remains basically unchanged. It belongs to the normal working stage. This stage is the wear life of the friction pair, which is generally the longest stage. It is also the key stage of lubrication management and equipment maintenance.
In this stage, the wear is slow and stable, and the wear rate remains basically unchanged. It belongs to the normal working stage. This stage is the wear life of the friction pair, which is generally the longest stage. It is also the key stage of lubrication management and equipment maintenance.
It is necessary to pay attention to the external environmental influence of the friction pair: such as water vapor ingress, external vibration source, etc.;
Select a suitable working lubricant inside the friction pair;
The technical ability of the equipment operator.
Select a suitable working lubricant inside the friction pair;
The technical ability of the equipment operator.
4. Severe wear stage
After a long period of stable wear, due to the change of the gap between the dual surfaces of the friction pair and the surface morphology and the fatigue of the surface layer, the wear rate increases sharply, resulting in a decrease in mechanical efficiency, loss of precision, abnormal vibration and noise, and a rapid increase in the temperature of the friction pair, which eventually leads to complete failure of the friction pair.
After a long period of stable wear, due to the change of the gap between the dual surfaces of the friction pair and the surface morphology and the fatigue of the surface layer, the wear rate increases sharply, resulting in a decrease in mechanical efficiency, loss of precision, abnormal vibration and noise, and a rapid increase in the temperature of the friction pair, which eventually leads to complete failure of the friction pair.
Before the friction pair increases sharply, some friction pairs can be repaired to avoid further deterioration, extend the service life of the friction pair, and postpone the period of severe wear. Such as manual repair of sliding bearings and repair of open gear tooth surfaces (using repair lubricants to repair the surface).